Evaluation of the laboratorial processes quality applied to titanium prostheses: plasma casting and laser welding - metallographic analysis / Avaliação da qualidade de processos laboratoriais aplicados nas próteses em titânio: fundição aplasma e soldagem a laser - análises metalográficas
Maria Cristina PEDRAZINI
Ronaldo Andrade Figueiredo OLIVEIRA
Sandra FABIANO
Antonio Marcos MONTAGNER
Thomaz WASSALL
Resumo
ABSTRACT
Objective
The aim of this study was to evaluate the quality of laboratory processes in titanium alloys.
Methods
Eight bars were cast using the voltaic arch technique. Three bars after casting were cut at three points and received, in total, nine laser welding points. All samples were analyzed under naked eye; 50X; 100X and 200X lens with electronic microscopy.
Results
All samples showed a perfect casting, without continuity solution or defects such as emptiness, bubbles, cracks, porosity or inclusions. The nine welding points didnt present any union failures, cracks or empty spaces and comparing this result with previous studies, there was improvement in the processes quality.
Conclusion
The good quality observed in these laboratorial processes were due to the improvement of the technicians learning curve, observation of the laboratorial protocols, the correction of possible defects in the equipment used and the application of statistical process control (SPC).
Indexing terms: Dental casting technique. Dental soldering. Titanium.
RESUMO
Objetivo
Avaliar a qualidade de processos laboratoriais aplicados em ligas de titânio.
Métodos
Oito padrões em cera foram fundidos com o uso da técnica de arco voltaico. Três barras, após fundidas, foram cortadas em três pontos gerando nove pontos de solda com a técnica a laser. Todas as amostras foram analisados a olho nú e em aumento de 50x, 100x e 200x usando microscopia eletrônica - análise metalográfica.
Resultados
Todas as amostras apresentaram boa fundição, sem soluções de continuidade, sem falhas como vazios, bolhas, trincas, porosidades e inclusões. Os nove pontos de soldas a laser não apresentaram falhas de união, trincas ou vazios e comparando estes resultados com achados anteriores, houve melhora na qualidade dos processos.
Conclusão
Conclui-se que a boa qualidade observada nesta investigação dos processos laboratoriais do titânio se deve tanto a melhora na curva de aprendizagem dos técnicos, observação dos protocolos laboratoriais como também correção dos possíveis defeitos nos equipamentos utilizados como também ao controle estatístico do processo (CEP).
Termos de indexação: Técnica de fundição odontológica. Soldagem em Odontologia. Titânio.
Texto completo: PDF
Ronaldo Andrade Figueiredo OLIVEIRA
Sandra FABIANO
Antonio Marcos MONTAGNER
Thomaz WASSALL
Resumo
ABSTRACT
Objective
The aim of this study was to evaluate the quality of laboratory processes in titanium alloys.
Methods
Eight bars were cast using the voltaic arch technique. Three bars after casting were cut at three points and received, in total, nine laser welding points. All samples were analyzed under naked eye; 50X; 100X and 200X lens with electronic microscopy.
Results
All samples showed a perfect casting, without continuity solution or defects such as emptiness, bubbles, cracks, porosity or inclusions. The nine welding points didnt present any union failures, cracks or empty spaces and comparing this result with previous studies, there was improvement in the processes quality.
Conclusion
The good quality observed in these laboratorial processes were due to the improvement of the technicians learning curve, observation of the laboratorial protocols, the correction of possible defects in the equipment used and the application of statistical process control (SPC).
Indexing terms: Dental casting technique. Dental soldering. Titanium.
RESUMO
Objetivo
Avaliar a qualidade de processos laboratoriais aplicados em ligas de titânio.
Métodos
Oito padrões em cera foram fundidos com o uso da técnica de arco voltaico. Três barras, após fundidas, foram cortadas em três pontos gerando nove pontos de solda com a técnica a laser. Todas as amostras foram analisados a olho nú e em aumento de 50x, 100x e 200x usando microscopia eletrônica - análise metalográfica.
Resultados
Todas as amostras apresentaram boa fundição, sem soluções de continuidade, sem falhas como vazios, bolhas, trincas, porosidades e inclusões. Os nove pontos de soldas a laser não apresentaram falhas de união, trincas ou vazios e comparando estes resultados com achados anteriores, houve melhora na qualidade dos processos.
Conclusão
Conclui-se que a boa qualidade observada nesta investigação dos processos laboratoriais do titânio se deve tanto a melhora na curva de aprendizagem dos técnicos, observação dos protocolos laboratoriais como também correção dos possíveis defeitos nos equipamentos utilizados como também ao controle estatístico do processo (CEP).
Termos de indexação: Técnica de fundição odontológica. Soldagem em Odontologia. Titânio.