Avaliação da resistência transversa de dentes acrílicos para base de dentaduras

Caio Gorgulho ZANET
Angela Guidini LOPES
Keren Cristina Kazue YUI
Rodrigo Máximo ARAÚJO
Márcia Carneiro VALERA
Maria Amélia Máximo ARAÚJO



Resumo

O destacamento de dentes anteriores nas próteses totais superiores ocorre com freqüência. Ultimamente têm surgido no mercado odontológico marcas comerciais de dentes acrílicos sem estudos quanto à resistência de união as bases de próteses. A proposta deste estudo foi verificar a resistência à força transversa de 3 marcas comerciais de dentes pré-fabricados em acrílico à uma base de resina termopolimerizável. Foram utilizados 30 dentes (incisivos centrais superiores), divididos em 3 grupos: A-Ivostar (Ivoclar Vivadent); B- Biotone (Dentsply) e Trilux (Ruthinium). Foi confeccionada uma retenção com ponta esférica na sua base e os mesmos foram unidos a um cilindro de resina acrílica termopolimerizável cor rosa (Clássico), obtidos a partir de técnica de inclusão de prótese total convencional e imersos em água destilada em estufa a 37o C por 7 dias. Em uma máquina de ensaios Instron (Universal 4301), foram aplicadas forças crescentes na face lingual, com angulação de 45o em relação ao longo eixo do dente, com velocidade de 0,5mm/min, até a ocorrência da fratura. Os valores obtidos foram submetidos ao teste estatístico ANOVA (=0,05) indicando que a tensão média de ruptura difere entre os grupos (F 2;27 = 215,22; p=0,001). O teste de Tukey mostrou diferença significante na resistência à força transversa dos dentes para as 3 marcas, em ordem decrescente (MPa): Ivostar (893,36  56,54), Biotone (593,58  68,11) e Trilux (342,5152,52). Concluiu-se que há diferenças estatisticamente significantes na resistência à força transversa de dentes pré-fabricados que devem ser levadas em consideração para a confecção das próteses.
Termos de Indexação:prótese parcial removível; prótese total superior; dente artificial


ABSTRACT
Detachment of anterior teeth from maxillary dentures is fairly frequent. Lately, several brands of acrylic teeth have been recommended to complete dentures fabrication. However, few studies may be found regarding bond strength between artificial teeth and acrylic bases. The purpose of this research was to quantify bond strength of 3 commercial brands of acrylic resin teeth to heat-cure resin denture base. Each group was composed of 10 teeth (maxillary central incisors) as follows A-Ivostar (Ivoclar Vivadent); B- Biotone (Dentsply) e Trilux (Ruthinium) adding up to 30 samples. All teeth were polished before mechanical retention was performed with round burs at the center of the ridge lap surface. The teeth were adapted to a cylindrical resin base (Clássico) obtained from heat-cured conventional polymerization technique. Samples were immersed into distilled water and stored at 37o C (7 days). Compressive test was performed (Instron 4301) applying an increasing load on the palatal surface at 45 degree angle to the long axis of each tooth. Load incidence was applied at a crosshead speed of 0,5mm/min until fracture occurred. Data obtained were submitted to ANOVA (=0,05) which demonstrated that the mean tension fracture rates were different among the groups (F 2;27 = 215,22; p=0,001). Tukey test verified statistically significant differences on adhesive bond strength of the three commercial brands (MPa): Ivostar (893.36  56.54), Biotone (593.58  68.11) e Trilux (342.5152.52). It can be concluded that statistical difference observed on adhesive bond strength of artificial teeth to resin bases should be considered prior to complete denture fabrication.
Indexing terms:removable partial denture; complete upper denture; artificial tooth


Texto completo: PDF



Research
Support Tool
  For this
avaliação pelos pares artigo
  Context
  Action

Capa | Atual | Arquivos | Sobre | Avisar | Contato | Buscar

RGO - Revista Gaúcha de Odontologia.   ISSN: 1981-8637